正交试验法在碱渣制备混凝土中应用

【作者】 李亚奇； 倪文； 徐东；

【Author】 LI YAqi;NI WEN;XU DONG;Civil and Environmental Engineering,University of Science and Technology Beijing;

【机构】 北京科技大学土木与环境工程学院；

【摘要】 采用正交试验方法对碱渣混凝土的配合比进行研究,考察了脱硫石膏、碱渣和钢渣的掺量对混凝土抗压强度影响情况。结果表明对混凝土抗压强度影响因素的大小为;脱硫石膏>碱渣>钢渣。对试验结果分析,调整各因素掺量的比例得出:在每立方需要400kg的胶凝材料的条件下,碱渣、石膏、钢渣掺量占胶凝材料总量的6%、12%、20%,保持水胶比在0.35,砂率为0.43的情况,可以制备出28天抗压强度达到60MPa的混凝土。更多还原

【Abstract】 Orthogonal test method of concrete mix soda residue study to examine the gypsum,caustic sludge and slag content influence the situation on the compressive strength of concrete.The results show that the compressive strength of concrete factors of size;gypsum>Alkali>slag.Analysis of the test results,adjust the dosage ratio derived factor:In every cubic 400 kg of cementitious material need to condition soda residue,gypsum,steel slag content accounted for 6%of the total cementitious material,12%,20%water cement ratio of 0.35,0.43 sand was the case,it can be prepared 28 days 60 MPa compressive strength of concrete.更多还原