【作者】 杨文； 常爱民； 杨邦朝；

【Author】 YANG Wen~(1,2),CHANG Aimin~(1,2),YANG Bangchao~2 (1.Xinjiang Institute of physics,Chinese Academy of Sciences,Urumqi, 830011;2.University of Electronic Science and Technology Si Chuan, Chengdu,610054,China)

【机构】 中国科学院新疆物理研究所； 电子科技大学信息材料工程学院；

【摘要】 采用溶胶-凝胶工艺制备了（Ba,Sr）TiO₃凝胶,并利用微波烧结技术对凝胶进行合成和烧结。结果表明,获得的（Ba,Sr）TiO₃粉体颗粒较细,与传统固相反应合成法相比,其钙钛矿相的合成温度由1100℃降至900℃;粉体的颗粒尺寸在50nm附近。更多还原

【Abstract】 The（Ba,Sr）TiO₃ powder was prepared by sol-gel processing and microwave sinter technique,their properties were studied and compared with the identical powder prepared by conventional technique.The results show that the synthetic temperature of the BST powder can be reduced from 1100℃to 900℃,The particle size of BST powder can be reduced from 320nm to 50nm.更多还原