纳米氧化铁粉体的制备和气敏性能研究
Investigation on Preparation and Gas Sensing Character of Nanocrystalline α-Fe2O3
【Author】 Li Jian Wang Yuansheng~+ Huang Zhaoxin (Department of Electronic Science and Applied Physics,Fuzhou University,Fuzhou,350002,China) (+ Central Laboratory,Fuzhou University,Fuzhou,350002,China)
【机构】 福州大学电子科学与应用物理系； 福州大学中心实验室；
【摘要】 本文以FeCl3·6H2O为源物质,研究用溶胶-凝胶法制备纳米级α-Fe2O3粉末,并制成烧结型直热式元件研究其气敏性能。气敏检测结果表明,该元件在功耗很低的条件下（45mW）,对CO气体具有很高的灵敏度和选择性以及较好的响应-恢复特性,其灵敏度在CO浓度为1000ppm时可达11,是常规CO气敏元件的两倍,因而适合于开发为高性能的CO气体传感器。
【Abstract】 The nanocrystallineα-Fe2O3 powder had been prepared by sol-gel method with FeCl3·6H2O as source material,and the gas sensing characters of the element made with the powder had been measured.With a very low power consumption of 45 mW,the element shows superior sensitivity and selectivity,and fairly good response-recovery characters to CO.The sensitivity to CO of 1000 ppm is measured to be 11,twice the value of the ordinary CO sensing element.Thus the powder is worthy to be further developed as the excellent CO sensing material.
- 【会议录名称】 第三届中国功能材料及其应用学术会议论文集
- 【会议名称】第三届中国功能材料及其应用学术会议
- 【会议时间】1998-10-13
- 【会议地点】中国重庆
- 【分类号】TB383.1
- 【主办单位】中国仪器仪表学会仪表材料分会、中国金属学会功能材料分会、中国化学会、中国物理学会发光分科学会、机械工业部重庆仪表材料研究所、北京有色金属研究总院、清华大学、中国科技大学、南京大学、吉林大学、东北大学、北京科技大学、天津大学、重庆大学、四川联合大学、电子科技大学、福州大学、北京航空航天大学、湖南大学、大连理工大学、华中理工大学、北京工业大学、合肥工业大学、《功能材料》编辑部、重庆市科学技术委员会