MLNi3.8Co0.6Mn0.55Ti0.05合金的微观结构与循环稳定性
The Microstructure and The Cycle Stability of MLNi3.8Co0.6Mn0.55Ti0.05 Alloy
【Author】 Li Chuanjian Wang Xinlin Wang Chongyu (Advanced Materials Institute,Central Iron & Steel Research Institute,Beijing,100081,China)
【机构】 冶金部钢铁研究总院新材料所；
【摘要】 通过电化学测量、显微组织分析研究了铸态和快淬的容量衰退及其机理。发现合金中的元素偏析导致的粉化、氧化加剧是铸态合金容量衰退的主要原因,而快淬合金可抑制元素偏析并使晶粒细化,基本上消除了循环过程导致的合金颗粒的粉化,从而提高合金的循环稳定性。提出合金的容量衰退机制有粉化一表面氧化和表面钝化两种机制,二者哪个起主要作用随制备合金工艺的不同而不同。
【Abstract】 The capacity decay of the as-cast and as-quenched alloys has been investigated by electrochemical measurement and microstructure observation.Segregation in the as-cast alloy can make alloy pulverize and oxidize fast,which plays the dominant role in capacity decay during cycling.The cycle stability is improved by quenching because segregaiton can be avoided and the grain size is very small in as-quenched alloy.There two main mechanism on the capacity decay,one is pulberization-oxidation,and the other is surface passivation. They play different role in different alloys made with different processing methods.
【Key words】 hydrogen-storage alloy； casting； quenching； cycíe stability； microstructure；