非晶态M1-Ni合金薄膜吸放氢性能的研究
Study on Property of Hydrogen Adsorption—Desorption of Amorphous M1—Ni Alloy Film
【Author】 Luo Daojun Hu Weikang Zhang Yunshi Wang Genshi (Institute of New Energy Material Chemistry,Nankai University,Tianjin,300071,China)
【机构】 南开大学新能源材料化学研究所；
【摘要】 本文用离子束溅射法合成了两种非化学计量比的非晶态Ml—Ni薄膜,用电化学方法研究其吸放氢性能,MlNi3.84与MlNi4.00合金薄膜的最大放电容量分别为165mAh/g和168mAh/g,薄膜不但具有良好的动力学性能,而且有很好的耐久性,在50mA/g电流密度下放电深度为100%时,循环寿命可达560次。
【Abstract】 In this paper two kind of nonstoichimetric amorphous M1-Ni alloy films are prepared by means of ion beam sputtering.Their hydriding and dehydriding property are investigated with electrochemical methods.The results shows that,the maximum hydrogen storage capacity is 165mAh/g for the M1Ni3.84 film and 168mAh/g for the M1Ni4.00 film,respectively. They also exhibit excellent hydriding-dehydriding dynamic characteristics,being able to sustain fast charging and discharging.In addition,the film has very good durability too,the life reaching 560 cycles under the conditions of the curent density of 500mA/g and the degree of discharge of 100%. But the self-discharge rate is really high.
【Key words】 ion beam sputering； nonstoichiometric； M1-Ni film； hydriding-dehydriding；