纳米稀土α-Fe2O3的气敏特性

Gas Sensitivity of Rare Earthα-Fe2O3

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具，请取消加速工具后下载。

【作者】 董立峰； 崔作林； 张志琨；

【Author】 Dong Lifeng Cui Zuolin Zhang Zhikun (Research Cenfer of Nanocrystalline Materials,Qingdao Institute of Chemical Technology,Qingdao,266042,China)

【机构】 青岛化工学院纳米材料研究所；

【摘要】 采用H2+Ar电弧等离子体法制备出纳米纯α-Fe2O3、Th-α-Fe2O3、Ce-α-Fe2O3,并研究其气敏特性。与无掺杂的纯α-Fe2O3相比,Th-α-Fe2O3对C2H2、C2H5OH的灵敏度明显提高,而Ce-α-Fe2O3则对C2H?OH的灵敏度明显增加,这与材料的微结构,尤其是材料表层的活性中心性质有关。

【Abstract】 Nanometer pureα-Fe2O3,Th-α-Fe2O3, Ce-α-Fe2O3 were prepared by H2+Ar arc plasma and their gas sensitivities were studied Compared with those of pureα-Fe2O3,the gas sensitivities of Th-α-Fe2O2 to C2H5,C2H5OH were higher,and the gas sensitivity of Ce-α-Fe2O3 to C2H5OH was much higher. The results showed that Th,Ce as additives not only increased the gas sensitivity,but also improved the selectivity. Th,Ce on the crystalline surface could effectively increase the surface active sites and lead to strong selective dissociation adsorption ability to reductive gases.

【关键词】 电弧等离子体； 气敏； 纳米； α-Fe2O3；
【Key words】 arc plasma； gas sensitivity； nanometer； α-Fe2O3；
  • 【会议录名称】 第二届中国功能材料及其应用学术会议论文集
  • 【会议名称】第二届中国功能材料及其应用学术会议
  • 【会议时间】1995-10-23
  • 【会议地点】中国四川成都
  • 【分类号】TB383.1
  • 【主办单位】中国仪器仪表学会仪表材料学会、中国金属学会材料科学学会、中国物理学会发光分会、中国光学学会薄膜专业委员会、机械工业部重庆仪表材料研究所、《功能材料》编辑部、大连理工大学、中国科技大学、北京科技大学、吉林大学、东北大学、中国科学院上海冶金研究所、中国科学院半导体研究所、北京大学、清华大学、南京大学、华中理工大学、武汉工业大学、电子科技大学、四川联合大学、西北工业大学、北京工业大学、东南大学、青岛化工学院、北京航空航天大学、山东工业大学
打印本页
节点文献中：