熔体快淬法制备纳米双相Nd10.1Fe76.2Co4.5Zr3B6.2永磁体

Melt-spun Nd10.1Fe76.2Co4.5Zr3B6.2 Permanent Magnet

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具，请取消加速工具后下载。

【作者】 王震； 倪建森； 徐晖； 吴义生； 黄照华； 侯雪玲；

【Author】 Wang Zhen, Ni Jiansen, Xu Hui, Wu Yisheng, Huang Zhaohua, Hou Xueling, Institute of Materials Shanghai University, Research Center of Nanoscience and Nanotechnolog Shanghai University, Shanghai 200072, China Nuclear Power Institute of China,Chengdu 510041, China

【机构】 上海大学材料研究所上海大学纳米科学与技术研究中心； 中国核动力研究设计院材科研究所；

【摘要】 Nd101.Fe76.3Co4.5Zr3B6.2合金经20m·s-1熔体快淬,在710℃/4 min退火处理后,制成的粘结磁体最佳磁性能为Br=7.02T,(?)Hc=739.4kA·m-1,(BH)(?)x=80.1kJ·m-3,加入Zr元素后,提高了该永磁材料的磁性能.

【Abstract】 Nd10.1Fe76.2Co4.5Zr3B6.2 magnet was prepared by melt-spun and subsequently annealed. After treated the ribbons at 710℃for 4 min, the mean grain size was 40-50nm. Excellent magnetic properties of the bonded magnet were achieved: Br=7.02T, JHC=739.4kA·m-1, (BH)max= 80.1kJ·3.The addition of Zr was found to improve the magnetic properties of bonded magnet.

【关键词】 熔体快淬法； 纳米晶； 粘结磁体； 磁性能； 稀土；
【Key words】 melt spun； nanocrystalline； bonded magnet； magnetic properties； rare earths；
【基金】 国家高技术研究发展计划(2002AA302602-2);上海市重点稀土材料开发及应用项目计划(03-111-54-05)
  • 【会议录名称】 第三届永磁及软磁铁氧体技术交流会论文集
  • 【会议名称】第三届永磁及软磁铁氧体技术交流会
  • 【会议时间】2004-10
  • 【会议地点】中国贵阳
  • 【分类号】TM273
  • 【主办单位】中国电子学会应用磁学分会
打印本页
节点文献中：