节点文献
可降解二氧化碳三元共聚物的研究
The research on degradable carbon dioxide tercopolymer
【Author】 HUANG Ke-long, LU Ling-bin, HUANG Lu(College of Chemistry and Chemical Engineering, Central South University, Changsha 410083, China; Hunan Chemical Engineering Institute, Changsha 410007, China)
【机构】 中南大学化学化工学院； 湖南化工研究院；
【摘要】 通过二氧化碳、环氧丙烷(PO)与γ-丁内酯(GBL)的三元开环共聚反应,得到一种新型的脂肪族聚碳酸酯亚丙酯丁内酯共聚物PPCG。对聚碳酸酯亚丙酯丁内酯的结构进行了FTIR、1HNMR、13CNMR表征,研究表明GBL被开环嵌入PO-CO2分子链中,使得共聚物中引入了易水解的羧酸酯单元。对PPCG的热性能、降解性能进行了研究。结果表明,在一定范围内,随着GBL单元的增加,特征黏度降低,玻璃态温度升高,材料降解性增强;不同的聚合反应时间对PPCG的特性粘度和玻璃态温度也有着明显的影响。
【Abstract】 A new aliphatic poly (propylene-co-γ-Butyrolactone carbonate) (PPCG) was successfully synthesized with terpolymerization of CO2, propylene oxide (PO) and γ-butyrolactone (GBL) by a macromolecule-bimetal complex (PBM) acting as catalyst. Its structure was determined by FTIR, 1HNMR and 13CNMR. The result showed that the ring of GBL was opened and inserted into the molecular chain of PO-CO2. GBL oFfered an aliphatic structural unit making the copolymer more hydrolysable. The PPCG copolymer exhibited a higher T8 than PPC. The influences of reaction time and ratio of PO:GBL (mol/mol) on Mv and Tg of copolymer were researched.
【Key words】 aliphatic polycarbonate； carbon dioxide； degradable； terpolymerization；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】O631.5
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部