对高温超导Ag基带再结晶织构的研究
Recrystal lization texture of sdilver substrate for high temperaturesuperconductor coatings
【Author】 LIU Xing, LIU Dan-min, LI Er-dong, MA Wei, ZHOU Mei-ling (College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022, China)
【机构】 北京工业大学材料学院；
【摘要】 通过对变形量为94.8%的Ag带在110℃不同时间下再结晶退火,并对其ODF和△ODF分析发现,Ag的再结晶是一个定向形核和长大的过程,再结晶时晶面基本保持不变,在晶面内晶向发生转动,分析可知在{023}面内{023}<301>∠蚴紫茸湮獅023}<123>∠蛉缓笤僮涑蓒023}<110>∠?在{110}面内,高斯、黄铜取向及{110}<311>∠虿欢霞跞踝湮獅110}<110>∠?所以控制冷轧取向集中在{110}面上,可以获得取向更为集中的{110}<110>∠?
【Abstract】 The silver tape with deformation of 94.8% undertook recrystallization annealings for different times at the temperature of 110℃. The recrystallization of the silver tape is a process of directional nucleaton and growth, with fixed crystal planes but rotared crystal orientations. The {023}<301>texture first turnsto {023}<123> then to {023}<110>on {023}plane through ODF and AODF, and Gauss texture, Brass texture and {110}<311>texture turn to the {110}<110>texture on the {110} plane. Therfore the silver tape with a strong {110}<110>texture can be obtained by a cold-rolling texture on {110} planes.
【Key words】 superconductor silver tape； recrystallization texture； texture； ODF；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TM26
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部