【Author】 PENG Gui-hua, JIANG Guo-jian, LI Wen-Ian, ZHUANG Han-rui (Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China)

【机构】 中国科学院上海硅酸盐研究所；

【摘要】 研究了不同起始反应物体系(Mg+Si,Mg2Si和Mg+Si3N4)对氮气中燃烧合成氮化硅镁(MgSiN2)粉体的影响,结果显示,不同反应物体系的燃烧产物不同.Mg2Si和Mg+Si3N4能获得单一相的MgSiN2,而且氧含量低至0.356%(质量分数),而Mg+Si体系燃烧产物除主相MgSiN2外,还含有少量Si和MgO及一些未知相.

【Abstract】 The new route to preparation of magnesium silicon nitride (MgSiN2) powder by combustion synthesis in nitrogen gas with several different starting mixtures (Mg+Si, Mg2Si, Mg+Si3N4) was investigated. The results showed that the compositions of the combustion products are different with different starting raw mixtures. Single-phase MgSiN2 powder can be fabricated from Mg2Si or the mixture of Mg and Si3N4 powder, and the oxygen content of the resulting powder is as low as 0.356wt%. However, the product by combustion synthesis from the mixture of Mg and Si in nitrogen gas consists mainly of MgSiN2 together with minor free Si, MgO and several unidentified phases.

【关键词】 自蔓延高温合成； 氮化硅镁；
【Key words】 self-propagating high-temperature synthesis； magnesium silicon nitride；
  • 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
  • 【会议名称】第五届中国功能材料及其应用学术会议
  • 【会议时间】2004-09
  • 【会议地点】中国北京·秦皇岛
  • 【分类号】TB44
  • 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部
打印本页
节点文献中：