Ni/SiO2介孔复合体的组装与光吸收性质研究

Investigation on assembly and optical absorption of Ni/SiO2 mesoporous composite

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具，请取消加速工具后下载。

【作者】 吴玉程； 程继贵； 解挺； 李广海； 张立德；

【Author】 WU Yu-cheng, CHENG Ji-gui, XIE Ting, LI Guang-hai, ZHANG Li-de(Faculty of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, China; Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031, China)

【机构】 合肥工业大学材料科学与工程学院； 中国科学院固体物理研究所；

【摘要】 采用溶胶-凝胶方法制备二氧化硅介孔固体,通过镍的硝酸盐溶液浸泡、干燥和随后氢热还原法,形成Ni/SiO2介孔复合体.根据DSC,XRD,TEM表征结果,纳米Ni颗粒尺寸为7-9nm,均匀地分布于SiO2介孔基体中.随着热处理温度提高.纳米颗粒尺寸增大,Ni/SiO2介孔复合体光吸收边明显发生红移.

【Abstract】 The silica mesoporous solids were produced by sol-gel method, and the Ni/SiO2 mesoporous composites were obtained through the processes from the immersion of nickel nitrate solution in the silica pores to dry treatment of the composites and sequent reducing heat treatment in H2 atmosphere. It was evidenced that the nanosized nickel in size of 7-9nm uniformly distributed in the silica matrix according to the characterization of DSC, XRD and TEM. Increasing with the heated temperature, the nanoparticles obviously grew that resuted in the red-shifting of the optical absorption edge.

【关键词】 Ni/SiO2； 介孔复合体； 组装； 光吸收性质；
【Key words】 Ni/SiO2； mesoporous composite； assembly； optical absorption；
【基金】 研究得到安徽省自然科学基金(00046403);安徽省“十五”科技攻关项目(01402007);合肥工业大学创新群体基金(纳米结构与功能纳米材料)支持.
  • 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
  • 【会议名称】第五届中国功能材料及其应用学术会议
  • 【会议时间】2004-09
  • 【会议地点】中国北京·秦皇岛
  • 【分类号】TB332
  • 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部
打印本页
节点文献中：