NDG-2镍基耐磨堆焊合金硬质相的研究
Study on hard phases of NDG-2 Ni based war-resistant overlaying alloy
【作者】 线恒泽；
【Author】 XIAN Heng-ze (Analvsis and Measurement Center, Harbin Institute of Technology, Harbin 150001, China)
【机构】 哈尔滨工业大学分析测试中心；
【摘要】 用恒流电解相萃取技术成功地提取了NDG-2镍基耐磨堆焊合金中主要硬质相Cr7C3、NiCrWSi,用XRD、SEM分析观察了堆焊合金中各种硬质相结构及结晶立体形态,探讨了硬质相对合金耐磨性能的影响.
【Abstract】 By means of constant-current electrolysis phase extraction, the main hard phases of Cr7C3, (Ni,Cr,W,Si) in NDG-2 Ni based wear-resistant overlag joint alloy were extracted successfu!ly,the structures and crystallized stereo-morphologies of hard phases in deposited alloy were observed by XRD and SEM, and the effect of hard phases on wear-resisting property of alloy was discussed.
【关键词】 耐磨堆焊；
电解相萃取；
硬质相；
镍基合金；
【Key words】 wear-resistant overlag joint； electrolysis phase extraction； hard phase； Ni base alloy；
【Key words】 wear-resistant overlag joint； electrolysis phase extraction； hard phase； Ni base alloy；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TG135.6
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部