稀土永磁材料Sm3（Fe,Ti,Co）29Nx

Permanent magnetic material Sm3（Fe,Ti,Co）29Nx

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具，请取消加速工具后下载。

【作者】 梁志梅； 崔春翔； 孙继兵；

【Author】 LIANG Zhi-mei, CUI Chun-xiang, SUN Ji-bing (School of Material Science and Engineering, Hebei University of Technology, Tianjin 300130, China)

【机构】 河北工业大学材料学院；

【摘要】 研究了Sm3(Fe,Ti,Co)29母合金的制备工艺,并对合金元素的选择及添加量进行了探讨。试验研究发现Ti元素可有效抑制α-Fe的生成并起到稳定Sm-Fe 3:29相的作用;熔炼时至少熔炼四遍可得到组织均匀的铸态试样;合理设计加料顺序可以减小Sm的挥发量,多加入20%-30%的Sm可有效的补偿Sm的挥发.成功的制备了Sm3(Fe,Ti,Co)29 3:29相母合金。

【Abstract】 The preparation of the mother alloy and the choice of the addition element and its amount were studied in this paper. It was found that the element Ti can prevent the formation of a -Fe efficiently and it is also a stable element for the formation of Sm-Fe-T 3:29 phase; the even structure of the as-cast alloy can be gained after melting at least four times; the evaporation of Sm can be reduced by adding different materials in a reasonable order, a surplus of 20% - 30wt% of Sm can compensate for the loss of Sm during melting properly. And the mother alloy Sm3(Fe,Ti,Co)29 were carried out in an electric arc furnace.

【关键词】 永磁材料； Sm3(Fe,Co,Ti)29Nx； HDDR；
【Key words】 permanent magnetic material； Sm3(Fe,Co,Ti)29Nx； HDDR；
【基金】 固家自然科学基金资助项目(50271024)
  • 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
  • 【会议名称】第五届中国功能材料及其应用学术会议
  • 【会议时间】2004-09
  • 【会议地点】中国北京·秦皇岛
  • 【分类号】TM273
  • 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部
打印本页
节点文献中：