共沉淀法合成纳米级YPO4:Tb及发光性能研究

Study on prepartion and the spectral property of nanosized YPO4 : Tb

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具，请取消加速工具后下载。

【作者】 韩燕； 牛淑云； 张洪武； 辛勤；

【Author】 HAN Yan, NIU Shu-yun, ZHANG Hong-wu, XIN Qin( Liaoning Normol University, Dalian 116029, China; Dalian Institute of Chemical Physics, Dalian 116023, China)

【机构】 辽宁师范大学化学化工学院； 大连化学物理研究所；

【摘要】 采用共沉淀法,以正丁醇为溶剂进行共沸蒸馏,合成了纳米级的YPO4:Tb,采用X射线衍射(XRD)、粒度分布和透射电镜(TEM)进行了表征并对发光性能进行了研究.实验结果表明合成的YPO4:Tb粒径大约为40nm左右,并且从其发射光谱中可以看出合成的纳米级YPO4:Tb有明亮的绿光发射.

【Abstract】 Nanosized YPO4: Tb was prepared by the methods of copricipation.It was studied by X-ray powder diffraction(XRD), Fourier transform (FT-IR) spectroscopy , luminescence spectra, and the distribution of nanosized particles was studied by cumulative particle size distribution curves. The experiment results show that the prepared YPO4 : Tb is about 40 nm. As a result the method of copricipation is a better way to prepare Nanostructured particles. The luminescence spectra of nanosized YPO4: Tb shows that it emits bright green.

【关键词】 共沉淀； 发光； 纳米粒子； YPO4:Tb；
【Key words】 copricipation； luminescence； nanostructured particles: YPO4: Tb；
【基金】 国家自然科学基金资助项目(90201018)
  • 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
  • 【会议名称】第五届中国功能材料及其应用学术会议
  • 【会议时间】2004-09
  • 【会议地点】中国北京·秦皇岛
  • 【分类号】TB383
  • 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部
打印本页
节点文献中：