Gd2O2S发光材料的长余辉发光行为
Long lasting photoluminescence of Gd2O2S phosphor
【Author】 MAO Da-li, ZHAO Xiao-lei, CHANG Cheng-kang, YING Wei-jiang( School of Materials Science and Engineering, Shanghai Jiaotong University, Shanghai 200030, China; Instrumental Analysis Center, Shanghai Jiaotong University, Shanghai 200030, China)
【机构】 上海交通大学材料学院； 上海交通大学分析测试中心；
【摘要】 使用固相合成技术制备了一系列Gd2O2S长余辉红色发光材料.在243nm紫外光激发下,具有很好的长余辉特性.这些发光材料具有多个发射峰,橙红色余辉发光是这些发射峰共同作用的结果.长余辉的形成是共激发离子Mg2+,Ti4+在Gd2O2S基质中形成一定浓度的电子陷阱的结果.在掺杂离子中,Ti4+的掺杂优于Mg2+的掺杂,而二者的共同掺杂获得了余辉特性更好的橙红色长余辉发光材料.
【Abstract】 Novel long lasting red phosphors, Eu3+ activated Gd2O2S co-activated with other ions, Mg2+ and Ti4+, were prepared by solid reaction method. XRD, luminescence spectrometer, thermal stimulated spectrometer were employed to characterize the obtained phosphors and to reveal the long lasting mechanism. The results obtained from the experiment show that, the Gd2O2S phosphors activated by Eu3+ will produce a red emission upon 243nm UV excitation, which is caused by a combined effect of the electron transition of Eu3+ from 5D excited states to 7F configurations. Long lasting behavior was observed for all samples prepared, due to an electron trap with suitable energy level formed within the oxysulfide matrix. The introduction of Ti4+ ion into the matrix exhibited better results than that of Mg2+, while the introduction of both the ions led to the best long lasting behavior.
【Key words】 phosphor； long lasting； oxysulfide； thermally stimulated luminescence；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB39
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部