The 50 nm-thick yttrium iron garnet films with perpendicular magnetic anisotropy

【摘要】 Yttrium iron garnet(YIG) films possessing both perpendicular magnetic anisotropy(PMA) and low damping would serve as ideal candidates for high-speed energy-efficient spintronic and magnonic devices.However,it is still challenging to achieve PMA in YIG films thicker than 20 nm,which is a major bottleneck for their development.In this work,we demonstrate that this problem can be solved by using substrates with moderate lattice mismatch with YIG so as to suppress the excessive strain-induced stress release as increasing the YIG thickness.After carefully optimizing the growth and annealing conditions,we have achieved out-of-plane spontaneous magnetization in YIG films grown on sGGG substrates,even when they are as thick as 50 nm.Furthermore,ferromagnetic resonance and spin pumping induced inverse spin Hall effect measurements further verify the good spin transparency at the surface of our YIG films.更多还原

【Abstract】 Yttrium iron garnet(YIG) films possessing both perpendicular magnetic anisotropy(PMA) and low damping would serve as ideal candidates for high-speed energy-efficient spintronic and magnonic devices.However,it is still challenging to achieve PMA in YIG films thicker than 20 nm,which is a major bottleneck for their development.In this work,we demonstrate that this problem can be solved by using substrates with moderate lattice mismatch with YIG so as to suppress the excessive strain-induced stress release as increasing the YIG thickness.After carefully optimizing the growth and annealing conditions,we have achieved out-of-plane spontaneous magnetization in YIG films grown on sGGG substrates,even when they are as thick as 50 nm.Furthermore,ferromagnetic resonance and spin pumping induced inverse spin Hall effect measurements further verify the good spin transparency at the surface of our YIG films.更多还原