【摘要】 研究了经单道次大应变热轧(LSR)和多道次小应变热轧(SSR)两种不同的轧制工艺下3mm的Mg-9Al-1Mn(AM91)挤压板的组织和性能。通过拉伸试验对两种工艺制备的板材的力学性能进行测定,并利用X射线衍射仪(XRD)、光学显微镜以及背散射电子衍射(EBSD)分析等方法对两种工艺制备的板材的微观组织进行观察和分析。研究结果表明:相比于SSR轧制态板材,LSR轧态及退火态的板材组织都得到了细化,织构也都得到了弱化,塑性变形能力得到了明显的改善。经LSR轧态的板材的断裂延伸率(FE)为20.5%,屈服强度(YS)为193MPa,抗拉强度(UTS)为284MPa。LSR工艺可显著改善板材的各向异性,SSR板材退火后的各向异性值(IPA)为8.8%,LSR板材退火后的IPA为5.0%。更多还原

【Abstract】 In this paper,the microstructure and mechanical properties of Mg-9 Al-1 Mn(AM91)alloy sheets,which processed by hot extrusion in 3 mm followed by single pass large strain hot rolling(LSR)and multi pass small strain hot rolling(SSR)were investigated.And the microstructure and properties of the sheets were examined by X-ray diffraction(XRD),optical microscope,electron back scatter diffraction(EBSD)and tensile test,respectively.The results showed that,compared with the SSR method,the finer grains and more weaken texture could be achieved via using the LSR method in the as-extruded AM91 alloy.Moreover,compared with the SSR sheet,the yield strength(YS),ultimate tensile strength(UTS)and fracture elongation(FE)of LSR AM91 sheet were 193 MPa,284 MPa and 20.5%,respectively.The plastic deformation capacity had been significantly improved.The mechanical anisotropy of the as-extruded sheet can be improved obviously by LSR method.The In-plane Anisotropy(IPA)of SSR and LSR AM91 sheet after annealing were 5% and 8.8%,respectively.更多还原