Synthesis and characterization of needle-like BaAl₂O₄:Eu,Dy phosphor via hydrothermal-homogeneous precipitation method

【摘要】 A needle-like Eu2+ and Dy3+ co-doped BaAl2O4 long-lasting phosphor was synthesized via a hydrothermal-homogeneous precipitation method assisted by cetyl trimethyl ammonium bromide(CTAB) as a template.The crystal structure,morphology and optical properties of the composites were characterized.XRD results showed that the single-phase BaAl2O4 was formed at 900 ℃ in an active carbon atmosphere,which was much lower than that prepared by traditional solid-state reaction method.Scanning electron microscopy(SEM) and transmission electron microscopy(TEM) observation revealed that the precursor had well-dispersed distribution and showed needle-like morphology with the average diameter of about 100 nm and the length up to 1 μm.The final product,BaAl2O4:Eu2+,Dy3+ phosphor,inherited the needle-like shape from precursor via adding the surfactant CTAB.After irradiation by ultraviolet radiation with 355 nm for 5 min,the phosphors emitted bluish green color long-lasting phosphorescence corresponding to the typical emission of Eu2+ ion.Both the photoluminescence spectra and luminance decay revealed that the phosphor had efficient luminescent and long-lasting properties.更多还原

【Abstract】 A needle-like Eu2+ and Dy3+ co-doped BaAl2O4 long-lasting phosphor was synthesized via a hydrothermal-homogeneous precipitation method assisted by cetyl trimethyl ammonium bromide(CTAB) as a template.The crystal structure,morphology and optical properties of the composites were characterized.XRD results showed that the single-phase BaAl2O4 was formed at 900 ℃ in an active carbon atmosphere,which was much lower than that prepared by traditional solid-state reaction method.Scanning electron microscopy(SEM) and transmission electron microscopy(TEM) observation revealed that the precursor had well-dispersed distribution and showed needle-like morphology with the average diameter of about 100 nm and the length up to 1 μm.The final product,BaAl2O4:Eu2+,Dy3+ phosphor,inherited the needle-like shape from precursor via adding the surfactant CTAB.After irradiation by ultraviolet radiation with 355 nm for 5 min,the phosphors emitted bluish green color long-lasting phosphorescence corresponding to the typical emission of Eu2+ ion.Both the photoluminescence spectra and luminance decay revealed that the phosphor had efficient luminescent and long-lasting properties.更多还原