Influence of flux treatment on the glass forming ability of Pd-Si binary alloys

【摘要】 Pd81Si19 amorphous alloys were prepared by combination methods of melt spinning and B2O3 flux treatment. A compari- son between the ribbons prepared from the fluxed ingots and the non-fluxed ones has been carried out. The result reveals that after fluxing treatment the glass transition temperature of the as-prepared glassy ribbons is reduced while the initial crystallization tem- perature is enhanced. It results in that the supercooled liquid region (defined as the difference between the initial crystallization tem- perature and the glass transition temperature) of the glassy alloy treated with fluxing technology has been increased from 31 to 42 K. This shows that fluxing technique can enhance the glass forming ability (GFA) of the binary alloy and improve the thermal stability of supercooled liquid of the glassy alloy.更多还原

【Abstract】 Pd81Si19 amorphous alloys were prepared by combination methods of melt spinning and B2O3 flux treatment. A compari- son between the ribbons prepared from the fluxed ingots and the non-fluxed ones has been carried out. The result reveals that after fluxing treatment the glass transition temperature of the as-prepared glassy ribbons is reduced while the initial crystallization tem- perature is enhanced. It results in that the supercooled liquid region (defined as the difference between the initial crystallization tem- perature and the glass transition temperature) of the glassy alloy treated with fluxing technology has been increased from 31 to 42 K. This shows that fluxing technique can enhance the glass forming ability (GFA) of the binary alloy and improve the thermal stability of supercooled liquid of the glassy alloy.更多还原