【摘要】 用中频磁控溅射工艺分别制备了掺铒Al2O3薄膜和镱铒共掺Al2O3薄膜,室温下测量了它们的光致发光特性。结果表明:镱铒共掺Al2O3薄膜光致发光的峰值强度为掺铒Al2O3薄膜的8倍以上,两者的半值宽度近似相等;泵浦功率增强,掺铒Al2O3薄膜光致发光强度出现饱和趋势,但镱铒共掺Al2O3薄膜的光致发光强度随泵浦功率线性增加。更多还原

【Abstract】 Er-doped Al₂O₃ films and Yb∶Er co-doped Al₂O₃ films were fabricated respectively using the technique of the medium frequency magnetron sputtering.The photoluminescent characteristics of the films were measured at room temperature.The results show that the PL peak intensity of the Yb∶Er∶Al₂O₃ film is eight times than that of the Er∶Al₂O₃ film,and the full width at half maximum of them is almost the same.The intensity of Er∶Al₂O₃ film trends to the saturation when pump power was increased.However,the intensity of （Yb∶Er∶Al₂O₃） film increases approximately linearly as pump power was increased.更多还原