【摘要】 研究了纳米m-ZrO₂颗粒初始含量对Al₂O₃为基体的复合材料烧结后所保留的四方相含量以及对硬度、断裂韧性和强度等力学性能的影响。随着纳米m-ZrO₂初始含量的增加，烧结样品中t-ZrO₂四方相的含量呈线性减少的趋势。纳米m-ZrO₂初始含量φ大于4％烧结样品显微硬度变化趋于稳定，当初始含量φ为4％时，样品的断裂韧性K_IC达到最大值5.84MPa·m^1/2，初始含量φ为2％时，断裂强度σf达到最大值395.0MPa，表明适量的纳米m-ZrO₂颗粒初始含量对Al₂O₃为基体的复合材料力学性能具有良好的改善作用。更多还原

【Abstract】 The present paper investigated the influence of nanometer m-ZrO₂ original contents on the reserved tetragonal phase, the hardness, the fracture toughness and the fracture strength for the sintered composites of m-ZrO₂ and Al₂O₃. The contents of t-ZrO₂ display the linear reducing trend with the increasing of nanometer m-ZrO₂ original contents. The micro-hardness of the sintered samples has the little change as the m-ZrO₂ original contents were over 4%. The fracture toughness K_IC and the fracture strength σ_f achieve the maximum values of 5. 84MPa · m^1/2 at the m-ZrO₂ original contents of 4 % and 395.0 MPa at that of 2% respectively. These results displayed the addition of the nanometer m-ZrO₂ was favorable to improve the mechanical properties of the composites based Al₂O₃ as the original contents of nanometer m-ZrO₂ was suitable.更多还原