【摘要】 报道一种新的中孔氧化铝催化材料的制备方法。通过该方法可以以无机盐和SB粉为原料经过沉淀、解胶的过程首先制得稳定的铝溶胶 ,然后经过干燥、焙烧得到中孔氧化铝催化材料。用BET ,TEM ,DTA和XRD等方法对该中孔氧化铝催化材料的基本物理化学性质进行了表征。实验结果表明在不使用模板剂的前提下 ,通过本文报道的方法能够制得比表面积较大、中孔分布集中的氧化铝材料 ,并且其孔径分布主要集中在 4nm左右。实验结果表明以SB粉为原料制备得到的氧化铝材料具有较好的热稳定性更多还原

【Abstract】 A novel sol gel process for preparing mesoporous alumina from precipitation and peptization process is reported in this article Inorganic salts and SB powder are used as raw materials in this study TEM, XRD, BET and DTA are used to characterize the properties of synthesized materials It is found that the mesoporous alumina materials with large specific surface area and narrow pore size distribution around 4?nm can be successfully prepared without using templates by present methods And the alumina material derived from SB powder has good thermal stability更多还原