【摘要】 研究了在 3.5 %NaCl溶液中带锈铸铁和 30 4不锈钢 (SS30 4)之间的电偶腐蚀效应和特性 ,以及面积比对电偶腐蚀效应的影响 .结果表明 ,SS30 4(面积为Ac)与带锈铸铁 (面积为Aa)面积比S(Ac/Aa)≤ 16时 ,电偶电流大小取决于SS30 4表面在耦合电位时的阴极反应速率 ;随着面积比S的增大 ,电偶电流密度Ig/Aa 增大 ,但Ig/Ac 降低 ,而且受限于SS30 4表面氧扩散极限电流密度 ;随面积比S的增大 ,电偶腐蚀效应增大 ,但相对来说 ,电偶腐蚀效应是较小的 .面积比S太大时 ,可能使本身为钝化态的SS30 4在偶接活化后发生阴极腐蚀 .建议S≤ 4.更多还原

【Abstract】 To know galvanic effect of aging iron artifacts and supporting stainless steel plate, galvanic corrosion characteristic of rusty cast iron and 304 stainless steel (SS304) in the 3.5%NaCl solution have been studied.The influence of area ratio of the two materials on the galvanic effect has also been investigated. The results indicate that the galvanic current of rusty cast iron and SS304 is dependent on cathodic reaction rate on the surface of SS304 at galvanic potential when SS304/rusty cast iron area ratio S ≤16. Furthermore,as the area ratio increases, galvanic current density I g/ A a increases. But I g/ A c reduces and is limited to oxygen diffusion limiting current density on the surface of SS304. With the increasing area ratio, galvanic effects rise but in general they are comparatively little in comparison with counterpart of common coupled metals. When the area ratio is too high, SS304, which is passive itself and then is activated after being coupled, may be suffer from cathodic corrosion. Therefore, area ratio S must not be too big in practical engineering. It is suggested that S ≤4.更多还原