【摘要】 用经γ射线辐照交联的ＰＥＯ作为固体电解质，研究了聚苯胺（ＰＡｎ）固态锂电他的电化学特性。实验发现通过γ－辐射交联后的ＰＥＯ电解质，室温电导率可达１０（－４）Ｓ／ｃｍ以上，并具有较好的机械强度。经过６８次的充放电循环实验、电池放电容量仍维持在６０ｍＡｈ／ｇＰＡｎ以上．该电池交流阻抗分析表明，界面Ｌｉ／ＰＥＯ的阻抗远大于界面ＰＥＯ／ＰＡｎ的阻抗．循坏伏安结果显示了聚苯胺具有良好的氧化还原可逆性．更多还原

【Abstract】 The electrochemical perforrnances of all- solid state lithium battery using polyani-line positive electrode and γ-ray crosslinked PEO electrolyte containing LiClO4/PC solutionhave been studied.It showed that the ambient temperature conductivity of PEO was over10(-4)S/cm as a result of γ-ray irradiation. The capacity of over 60mAh/g and the charge- dis-charge life of over 68 cycles were achieved for the polyaniline lithium battery. The acimpedance at the Li/PEO interface was much greater than that at PEO/PAn. The result ofcyclic voltammetry showed good reversibility of the polyaniline electrode in the lithium bat-tery.更多还原