The effect of yttrium oxide dispersoid distribution on the 980℃ rupture life of an ODS nickel-based superalloy MGH 754 was investigated.The block accumulation of oxide dispersoid because of being not complete of MA process results in cavity production on grain boundaries. By improving MA process , the block accumulation of oxide dispersoid can be eliminated and the high temperature rupture property can be improved.