Ni55.30Fe17.60Ga27.10磁致形状记忆合金马氏体相变
Martensitic transformation of Ni55.30Fe17.60Ga27.10 magnetic shape memory alloy
【Author】 ZHENG Hong-xing, XIA Ming-xu, LU Yu-ying, LIU Jian, LI Jian-guo (School of Materials Science and Engineering, Shanghai Jiaotong University, Shanghai 200030, China)
【机构】 上海交通大学材料科学与工程学院；
【摘要】 研究了热处理对Ni55.30 Fe17.60 Ga27.10磁致形状记忆合金组织和马氏体相变的影响。电弧态合金组织中马氏体板条模糊.在氩气保护,800℃保温4h缓慢冷却条件下热处理后,马氏体板条规整平直.DSC结果表明:Ni55.30Fe17.60Ga27.10合金在加热/冷却时发生热弹性马氏体相变。热处理后Ms=43.24℃,Mf=36.72℃.As=46.84℃,Af=51.83℃.相比电弧态,热处理后合金Ms和Mf提高,As和Af降低,相变滞后减小。XRD结果证明热致马氏体为14M马氏体.
【Abstract】 Effect of heat treatment on the microstructures and martensitic phase transformation of Ni55 30Fe,7.60Ga27.10 alloys was studied. Ni55.30Fe17.60Ga27.10 alloys underwent a thermoelastic martensitic transformation during heating and cooling. The boundaries of martensitic variants of arc-melted Ni55.30Fe17.60Ga27.10 alloys were blurring, and after heating 800℃ for 4h under the Ar atmosphere, the martensitic variants became distinct and straight. DSC results shown that the characteristic temperatures of martensitic transformation, Ms, Mf, As and Af, were 43.24℃, 36.72℃, 46.84℃ and 51.83℃, respectively. Compared with arc-melted alloy, the temperatures, Ms, and Mf, increased slightly, and on the contrary, A, and At decreased slightly, and the heat hysterisis became smaller. XRD verified the martenstte was 14M structure.
【Key words】 Ni-Fe-Ga alloy； magnetic shape memory； martensitic transformation；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TG139
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部