Synthesis and microstructure of thermotropic copolyester/ MMT nanocomposites
【Author】 GUO Zhao-ying, MAO Lian-bo, XIE Xiao-lin, ZHOU Xing-ping, ZENG Fan-di (Department of Chemistry, Huazhong University of Science and Technology, Wuhan 430074, China)
【机构】 华中科技大学化学系；
【摘要】 采用一定量的有机蒙脱土和40 mol%的聚对苯二甲酸丁二酯(PBT)与60 mol%的对羟基苯甲酸(p-HBA)的原位乙酰化法反应,制备了PBT40-PHB60热致液晶共聚酯/蒙脱土纳米复合材料。实验结果表明液晶共聚酯和蒙脱土之间存在强烈的相互作用,蒙脱土以完全剥离的形态分散于液晶高分子形成了全剥离型的热致液晶共聚酯/蒙脱土纳米复合材料,其中LCP仍然表现出原有的向列型液晶行为,但液晶微区随蒙脱土含量的增加而明显细化,纹影结构的向错点也变得模糊。
【Abstract】 The liquid crystalline copolyester (LCP)/montmorillonite (MMT) nanocomposites were synthesized with 40 mol% poly (butylene terephthalate) (PBT), 60 mol%p-hydroxybenzoic acid (PHB) in the presence of organoclay by in-situ acetylation. The results showed that LCP macromolecules entered the galleries of the organoclay, and fully-exfoliated LCP/clay nanocomposites were fabricated. Due to the strong interaction between LCP and exfoliated MMT layers, the incorporation of the exfoliated MMT layers throughout the LCP matrix results in very fine but imperfect schlieren texture, and the disinclination becomes blurred.
【Key words】 liquid crystalline copolyester； organized montmorillonite； nanocomposites； exfoliation；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB332
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部