溶胶凝胶法制备LaF3超细粉的实验研究
Study on the LaF3 superfine powder by sol-gel method
【作者】 韩元山； 田彦文； 王常珍； 吴玉锋； 安守勇； 翟玉春；
【Author】 HAN Yuan-shan, TIAN Yan-wen, WANG Chang-zhen, WU Yu-feng, AN Sou-yong, ZHAI Yu-chun (School of Materials & Metallurgy, Northeastern University, Shenyang 110004, China,)
【机构】 东北大学材料与冶金学院；
【摘要】 采用La(CH3COO)3、NH4F为基本合成原料,通过单因素的实验方法考察了反应物的浓度、搅拌强度、滴加速度和溶液的PH对形成稳定LaF3溶胶的影响。其最佳的制备工艺条件为:La(CH3COO)3浓度为0.005mol·L-1(NH4F浓度为相应的La(CH3COO)3浓度的3倍),高速搅拌强度、滴加速率为60滴/man,NH4F溶液的pH值为6。此溶胶经过微波加热离心分离得到LaF3凝胶,凝胶经过微波加热烘干研磨,所制得的LaF3超细粉。经过X-ray和SEM证明,其纯度较高且平均拉径为250nm。
【Abstract】 The influence of different experimential condition has been investigated in the process of preparing LaF3 colloidal sol by La(CH3COO)3 and NH4F. The optimum conditions: La(CH3COO)3concentration is 0.005mol·L-1 and NH4F is 3 times than La(CH3COO)3; stiring speed is very high ;drop speed is 60d/min, NH4F solution pH is 6. LaF3 superfine powder has also been prepared by centrifugal separating, microwave heat, grind. The LaF3 superfine powder is very pure and small (250nm) proved with X-ray and SEM.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB44
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部