Ti-O薄膜的溅射刻蚀微形貌表面对内皮细胞生长的影响
Effect of surface micromorphology of ti-o film etched by sputtering on biological behavior of endothelial celis
【Author】 TIAN Ren-lai, HUANG Nan, CHEN Jun-ying, LENG Yong-xiang, WANG Lu (School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031, China; Key Laboratory of Advanced Technologies of Materials, Ministry of Education, Chengdu 610031, China)
【机构】 西南交通大学材料先进技术教育部重点实验室； 四川省人工器官表面工程重点实验室；
【摘要】 利用磁控溅射合成具有一定特性的Ti-O薄膜。并采用Ar离子溅射刻蚀该薄膜表面.运用原子力显微镜(AFM),X射线衍射(XRD)对刻蚀后的薄膜表面微现形貌、微结构进行表征.结果表明:薄膜的结构未发生变化,表面的粗糙度减小.进一步的人脐静脉内皮细胞(HUVEC)种植实验表明:表面粗糙度的变化对内皮细胞的贴附、生长与增殖有很大的影响.
【Abstract】 In this work, Ti-O films was synthesized by magnetron sputtering and etched subsequently by Ar ion. The micromorphology, structure of the films were investigated by Atomic force microscope (AFM) and X-ray diffraction (XRD), respectively. The biological behavior of cultured human umbilical vein endothelial celis (HUVECs) onto different film surface morphology were investigated by the in vitro HUVECs cultured experiment. The analysis results showed that the surface roughness of etched films is lower, but the structure of films is uninfluenced. Our in vitro EC culture investigation indicated that the biological behavior such as the adherence, growth and proliferation etc of the ECs is obviously different due to the different surface topography of films
【Key words】 magnetron sputtering； etching； Ti-O film； surface morphology； endothelial celis；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】R318.1
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部