HDDR处理的Sm2Fe16Ti1Nx化合物高能球磨的研究
Effect of high-energy ball-milling process on the Sm2Fe16Ti1Nx compounds prepared by HDDR
【作者】 孙继兵； 崔春翔； 崔静； 王如； 张颖； 梁志梅；
【Author】 SUN Ji-bing, GUI Chun-xiang, GUI Jing, WANG Ru, ZHANG Ying, LIANG Zhi-mei (School of Material Science and Engineering, Heibei University of Technology, Tianjin 300130, China)
【机构】 河北工业大学材料学院；
【摘要】 在用HDDR法制备Sm2Fe16Ti1Nx氮化物过程中,研究了高能球磨对氮化物粉末的形貌、物相结构及磁性能的影响。发现高能球磨Sm2Fe16Ti1Nx氮化物使粉末颗粒细化的过程可描述为:大粉末颗粒→压延成层片状→断裂成短棒状及球形颗粒→压延成层片状→断裂成球形小颗粒,并在球磨一定时间后使粉末中的Sm2(FeTi)17Nx主相完全非晶化,a-Fe含量增高且没有非晶化。球磨后粉末的矫顽力随着球磨时间的延长而降低,而剩磁在球磨短时间时降低,再延长球磨时间又增高,在球磨较长时间到Sm2(FeTi)17Nx主相完全非晶化后又使剩磁降低,最高磁场下的磁化强度值则随着球磨时间的延长而增加。手研磨后粉末的矫顽力随研磨时间的延长而逐渐升高而剩磁及最高场下磁化强度值变化不大。
【Abstract】 The effect of high-energy ball-milling and grinding on the powder shape and size, microstructure and magnetic properties of Sm2Fe16Ti1Nx nitride prepared by HDDR was investigated. It was shown that the steps to break up Sm2Fe16Ti1Nx powders by high-energy ball-milling can be described as : bigger powder particles-calendering to form layer particles-breaking to stub or sphere particles-calendering to form layer particles-finer particles. The process of Ball-milling longer time promoted the Sm2(Fe,Ti)17Nx phase to became amorphous phase thoroughly and increased the content of a -Fe, but no whole amorphous a -Fe was found. The coercivity of nitrides by ball-milling was decreased with increasing ball-milling time, the remanence become lower within shoner ball-milling time such as 2h and then increased with increasing milling time, at length, the remanence decreased to the minimum value when ball-milled longer time. On the contrary, magnetization at maximum magnetic field was increased with increasing ball-milling time. Compared with high-energy ball-milling, the coercivity of abrasive Sm2Fe16Ti1Nx was improved with increasing grinding time and the remanence and magnetization changed little.
【Key words】 Sm2Fe16Ti1Nx； high-energy ball-milling microstructure； phases； magnetic properties；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TF123
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部