溶胶凝胶模板法制备钴铁氧体纳米线、纳米管
Synthesis of CoFe2O4 nanowires and nanotubes by a sol-gel template method
【作者】 姬广斌； 任尚坤； 唐少龙； 徐宝龙； 顾本喜； 都有为；
【Author】 JI Guang-bin, REN Shang-kun, TANG Shao-long, XU Bao-long, GU Ben-xi, DU You-wei(National Laboratory of Solid State Microstructure and Physics Department,Nanjing University, Nanjing 210093, China)
【机构】 南京大学固体微结构国家重点实验室；
【摘要】 利用溶胶凝胶模板方法,通过控制不同的退火工艺成功制备出平均直径约40 nm的COFe2O4纳米线和纳米管,振动样品磁强计(VSM)测试结果表明样品的矫顽力随退火速度的增加而降低。
【Abstract】 CoFe2O4 nanowires and nanotubes with an average diameter of about 40 nm were prepared in porous anodic aluminum oxide (AAO) template using sol-gel process. Transmission electron microscopy (TEM) diffraction pattern and X-ray diffraction (XRD) showed that the nanowires were polycrystalline phase. The effect of heating rate on the structure and magnetic properties of CoFe2O4 nanowires and nanotubes were investigated. The result showed that the coercivity decreased with the increase of the heating rate.
【Key words】 AAO template； sol-gel processing； CoFe2O4； nanowires； nanotubes；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部