NiMnSb半金属材料的制备、磁性和电输运特性
Preparation and magnetic electronic transport properties of NiMnSb half metallic materials
【Author】 REN Shang-kun, JI Guang-bin, HUANG Song-ling, ZHANG Feng-ming, DU You-wei (National Laboratory of Solid State Microstructures, Nanjing University, Nanjing 210093, China)
【机构】 南京大学固体微结构国家重点实验室；
【摘要】 报道了NiMnSb半金属材料的一种简单方便的制备方法。分析了烧结温度对材料结构特征的影响。结果表明600-800℃的温度烧结4h为较佳的烧结条件。通过研究发现,在300K以下温度区域的磁性行为和Heisenberg铁磁体局域电子模型的经典自旋波理论的预言相符合,遵循温度的T3/2变化规律;在高场磁化过程中,磁硬度系数和磁各向异性随温度的变化反映出材料的内应力和各向异性随温度的变化规律;电阻率随温度的变化关系满足温度的T1.35规律。
【Abstract】 A new synthesizing method of NiMnSb materials was reported, which is simple and convenience. The effects of sintering temperature on structures of NiMnSb materials were analyzed. It is found that the sintering conditions of at the temperature range from 600-800℃ for 4 h are the best process. The magnetic and transport properties of half-Heusler NiMnSb half-metallic ferromagnetic materials were studies. It is found that in the temperature range of below 300K, the magnetic behavior of NiMnSb is in according with the prediction of classical spin wave theory of Heisenberg ferromagnetic localization mode. The variations of magnetization with the temperature are following the T3/2 law. The magnetic rigidity coefficient and anisotropy constant are varying in some special laws with temperature. The resistivity is as function of temperature, which varying is following the T1.35 law.
【Key words】 half-metallic； magnetization； ferromagnetism； NiMnSb； spin-electronics；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB34
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部