SrBi2Nb2O9的PLD制备及其非线性光学特性
The nonlinear optical properties of SrBi2Nb2O9 thin films by pulsed laser deposition
【Author】 SONG Rui, GU Hao-shuang, WANG Zhong-tai, CHEN Kan-song, ZHANG Tian-jin (Faculty of Physics & Electronic Technology, Hubei University, Wuhan 430062, China)
【机构】 湖北大学物理学与电子技术学院；
【摘要】 利用脉冲激光沉积(PLD)方法在MgO(100)基片上生长了SrBi2Nb2O9薄膜.XRD分析表明在MgO基片上生长的薄膜呈(115)单一取向,具有良好的结晶性;XPS数据分析得到薄膜中Sr、Bi和Nb的原子比约为1:2:2.05。利用Z扫描技术对薄膜的三阶非线性光学性质进行了测量,通过开孔(Open-aperture)和小孔(Close-aperture)的测量,计算出三阶非线性光学极化率的实部Rex(3)和虚部Imx(3)分别为4.139×10-7esu,1.104×10-7esu.
【Abstract】 SrBi2Nb2O9 (SBN) thin films were prepared on MgO(100) substrates by the pulsed laser deposition technique. The x-ray diffraction (XRD) data indicate that the films are highly (115) orientation. The atomic ratio of Sr:Bi:Nb derived from the XPS data was 1:2:2.05. A single beam Z-scan determined the nonlinear optical properties of the films. The open-aperture and closed-aperture results show that SBN thin films exhibit a nonlinear optical response with the real and imaginary parts of the third-order nonlinear optical susceptibility being 4.139×10-7 esu and 1.104×10-7 esu, respectively.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB34
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部