【摘要】 利用三明治电池和伏安法测试了不同制备条件的Nafion基氧化还原聚合物膜在空气中的电荷传输性能.研究结果表明,混合适量聚乙二醇(PEG)的Nafion基金属联吡啶配合物｛Nafion[M(bpy)23+,PEG](M=Ru,Fe)｝膜的表观电荷传递扩散系数(Dct)达到10-6-10-7cm2·s-1,电子或空穴迁移率(μ)达到10-4-10-5cm2·V-1·s-1.在导电玻璃(ITO)电极与Nafion基氧化还原聚合物膜界面引入一层导电聚苯胺(PANI)后,降低了其接触电阻,使氧化还原聚合物膜的Dct提高至10-5-10-6cm2·s-1,μ提高至10-3-10-4cm2·V-1·s-1,且工作电流提高了近两个数量级.该固态氧化还原聚合物膜的性能比较稳定,在空气中放置30天后其Dct和μ降低得很少.更多还原

【Abstract】 The charge transport performance of the Nafion-based redox polymer films prepared under different conditions was investigated by cyclic voltammetry in the sandwiched cells.The results showed that the apparent charge transfer diffusion coefficient(Dct)of the Nafion[M(bpy)2+3,PEG(polyethylene glycol)](M=Ru or Fe)films is about 10-6-10-7 cm2·s-1 and the mobility of the electron or hole(μ)was about 10-4-10-5 cm2·V-1·s-1.In order to decrease the resistance of the interface,a polyaniline(PANI)layer was added to the interface of indium tin oxide coated conducting glass(ITO)electrode and the redox polymer.Consequentially,the Dct could be increased to about 10-5-10-6 cm2·s-1 and μ to about 10-3-10-4 cm2·V-1·s-1,and the operating current of the cells under 600 mV bias could be increased by almost 100 times.In addition,the Dct and μ of this redox polymer film had just reduced slightly after 30 d kept in atmosphere.Therefore,the redox polymer film is sufficiently stable.更多还原