【摘要】 在无催化剂的条件下,利用碳热还原反应气相沉积法制备出了高产率单晶Sn掺杂ZnO纳米带.XRD和TEM研究表明纳米带为结晶完好的纤锌矿结构,生长方向沿[0001],EDS分析表明纳米带中Sn元素含量约为1.9%.室温光致发光谱(PL)显示掺锡氧化锌纳米带存在强的绿光发射峰和较弱的紫外发射峰,谱峰峰位中心分别位于494.8nm和398.4nm处,并对发光机制进行了分析.这种掺杂纳米带有望作为理想的结构单元应用于纳米尺度光电器件领域.更多还原

【Abstract】 Single crystalline Sn-doped ZnO nanobelts were successfully synthesized by the carbon thermal reduction deposition process without using any catalyst. XRD investigation confirmed that the products were the wurtzite structure of ZnO. SEM, EDS, and TEM analyses showed that the Sn-doped ZnO nanostructures contained a belt-like morphology with Sn doping content about 1.9%, and the growth direction of nanobelts was along the [0001] direction. A weak UV emission peak at around 398.4 nm and a strong green emission peak at around 494.8 nm were observed at room temperature. The luminescence mechanism of the Sn/ZnO nanobelts was also discussed. These nanobelts were promising building blocks for fabrication of nanoscale optoelectronic devices.更多还原