【摘要】 目的:研究光固化树脂加强型玻璃离子黏结剂与自酸蚀光固化正畸黏结剂对金属托槽-牙面黏结的特点。方法:60颗离体前磨牙随机分成6组,每组10颗牙,3组用光固化树脂加强型玻璃离子黏结剂,另3组用自酸蚀光固化复合树脂黏结剂黏结正畸托槽,分别于0.5、24h及冷热循环实验后测试其抗剪强度及黏结剂残留指数,并通过扫描电镜观察树脂—牙釉质面形态。结果:2种材料黏结强度均能超过5MPa。但是,24h自酸蚀光固化正畸黏结剂的强度高于光固化树脂加强型玻璃离子黏结剂的强度(P<0.05)。结论:2种光固化正畸黏结剂能提供正畸临床黏结金属托槽足够的黏结力。更多还原

【Abstract】 Objective: To investigate the adhesive characteristics of two kinds of light-curing resin that was used to bond teeth and orthodontics brackets. Methods: A total of 60 premolar teeth were randomly divided into six groups, and brackets were bonded according to the manufacturers’ instructions. In group A1, A2 and A3, the teeth were prepared using 100 ml/L polyacrylic acid, and the brackets were bonded using Fuji Ortho LC. In group B1, B2 and B3, the teeth were using self-etching primer, and the brackets were bonded using Transbond Plus Self Etching Primer (TPSEP). After 30 min and 24 h under room temperature and received cold-heat cycle treatment respectively, bond strength was measured using a testing instrument (2000S, Lloyds Instruments, Fareham, England) at a speed of 1 mm/min, and the residual adhesive was quantified using a stereomicroscope. The adhesive interface was observed by scanning electron microscope. Results: The bond shear strength of TPSEP and Ortho Glass LC are more than 5 MPa. The bond shear strength of TPSEP is stronger than that of Ortho Glass LC after 24 h. However,The adhesive remnant index (ARI)of TPSEP is higher than that of Ortho Glass LC. Conclusion: Transbond Plus Self Etching Primer and Ortho Glass LC can satisfy the clinic need of orthodontics.更多还原