PLZT纳米薄膜的制备及其特性研究

Preparation and Properties of PLZT Nanometer Thin Film

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 SU Jie1,YU Da-shu1,GUO Yun-feng3,HE Ju2,WANG Li-qun1 (1.College of Physics and Electronic Information Science,Tianjin Normal University,Tianjin 300074,China;2.Department of Applied Physics,Faculty of Science,Tianjin University,Tianjin 300072,China;3.Department of Electronic Information,Huangshan University,Huangshan 245041,China)

【机构】天津师范大学物理与电子信息学院；天津大学理学院应用物理系；黄山学院电子信息工程系；天津师范大学物理与电子信息学院天津300074；天津300074；天津300072；黄山245041；

【摘要】经溶胶-凝胶法制备出PLZT纳米多层膜,采用热重-差热、X射线衍射、拉曼光谱、SEM等对目标产物进行性能和微结构分析。结果表明:在700℃下保温30min,得到粒径约为50～70nm钙钛矿结构的PLZT纳米薄膜,随Zr含量增大粒径变小,且由三方相向四方相转变。更多还原

【Abstract】 The Pb0.93La0.07(ZrxTi1-x)0.93O3(abbreviated as PLZT) thin film was prepared by Sol-gel process.The samples were investigated by TG-DTA,XRD,Rama spectrum and SEM.The results show that the PLZT nanosized thin film with perovskite structure in size of about 50-70nm was obtained at 700℃ sintering for 30min,The particle size of PLZT nanosized thin film decreases and the phases of PLZT nanosized thin film shifts from tetragonal to thombohedral with the increasing of the Zr concentration.更多还原

【关键词】溶胶-凝胶法；不同Zr/Ti比； PLZT纳米薄膜；
【Key words】 Sol-gel process； different Zr/Ti； PLZT nanosized film；

【基金】天津市高等学校科学发展基金(No.20041022);天津师范大学青年科研基金(No.52LJ39);天津师范大学自然科学基金(No.5RL019)资助项目

【文献出处】人工晶体学报 ,Journal of Synthetic Crystals , 编辑部邮箱 ,2007年03期

【分类号】TN304
【被引频次】2
【下载频次】195

知网节下载

节点文献中：

本文链接的文献网络图示:

本文的引文网络

节点文献