SmCo薄膜的共溅射制备及磁学性能研究

Studies on the Preparation and the Magnetic Property of SmCo/Cr Thin Films with Co-sputtering

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 WANG Hui,HUANG Zhi-xin,WU Bin,ZHANG Feng,LIU Min,ZHANG Yu-long,ZHANG Ping(1.Dept.of Physics,Huazhong Normal University,Wuhan 430079,China;2.Dept.of Physics and Engineering electronics,Yunyang Teacher’s College,Danjiang kou 442700,China)

【机构】华中师范大学物理科学与技术学院；郧阳高等师范专科学校物理与电子工程系；郧阳高等师范专科学校物理与电子工程系武汉430079；武汉430079；丹江口442700；

【摘要】采用磁控共溅射方法制备了非晶态的SmCo磁性薄膜,用振动样品磁强计(VSM)分析了薄膜的磁学性能,并通过原位后退火处理研究了其磁学性能。结果表明,在600℃下退火30分钟,SmCo薄膜样品的矫顽力升高,并且磁化取向有从面内转向垂直方向的趋势。更多还原

【Abstract】 Amorphous SmCo magnetic films were fabricated by magnetron co-sputtering method and the magnetic properties were measured by a vibrating sample magnetometer(VSM).Through in-site post annealing,the magnetic properties of the SmCo thin films were investigated.The results shows that after 600 ℃,30min annealing,the coercivity of SmCo films will be increased and the magnetic anisotropy will be changed from in-plane to normal-plane.更多还原

【关键词】 SmCo薄膜；共溅射；退火；矫顽力；
【Key words】 SmCo film； co-sputtering； annealing； coercivity；