Influence of electromagnetic stirring on microstructure of AZ91-0.8%Ce magnesium alloy

【Abstract】 Effect of electromagnetic stirring on microstructure of AZ91-0.8%Ce magnesium alloy was investigated. The results show that electromagnetic stirring causes a change of morphology of α-Mg phase from coarse dendrites to fine rosette-like or spherical shape. Grain size is significantly refined within the range of input voltage 75?125 V, moreover, the optimum input voltage corresponded to the minimum value (64 μm) of grain size is 125 V. Compared to the non-stirred condition, the amount of β-Mg17Al12 precipitate under the stirred condition obviously increases. The grain refinement of AZ91-0.8%Ce alloy is mainly attributed to multiplication of existing grains in the melt caused by forced fluid flow under electromagnetic stirring condition. Addition of 0.8% Ce results in the formation of ‘necking’ at secondary dendrite arm roots of α-Mg crystals, and consequently, it is helpful to increase the number of heterogeneous nucleation.更多还原