Synthesis and Luminescence Properties of Red Phosphors:Mn²⁺ Doped MgSiO₃ and Mg₂SiO₄ Prepared by Sol-Gel Method

【摘要】 <正>Sol-gel method was utilized to synthesize two different series of red silicate phosphors : MgSiO3 and Mg2SiO4 powder samples doped with Mn2+, conducted the investigation of red long-lasting phosphor: MgSiO3 : Eu2 + , Dy3+, Mn2+ . TGA curves of the gel precursor for two series depicted that the loss of residual organic groups and NO3 groups occurs below 450℃. According to the XRD patterns, the major diffraction peaks of the MgSiO3 and Mg2SiO4 series are consistent with a proto-enstatite structure (JCPDS No.11-0273) and a forsterite structure (JCPDS No.85-1364) respectively. With the excitation at 415 nm, the red emission band of Mn2+ ions is peaked at 661 nm for MgSiO3:1%(atom fraction) Mn2+ or 644 nm for MgiSiO4: 1 %(atom fraction) Mn2+ . Compared with Mg2SiO4:Mn2+ samples, MgSiO3:Mn2+ samples exhibit higher luminescence intensity and higher quenching concentration. In addition, the two series co-doped with Eu2+ , Dy3+ , Mn2+ were also prepared. Photo-luminescence and afterglow properties of the two co-doped series were analyzed, which show that MgSiO3: Eu2 + , Dy3+ , Mn2+ is more suitable for a red long-lasting phosphor.更多还原

【Abstract】 Sol-gel method was utilized to synthesize two different series of red silicate phosphors : MgSiO3 and Mg2SiO4 powder samples doped with Mn2+, conducted the investigation of red long-lasting phosphor: MgSiO3 : Eu2 + , Dy3+, Mn2+ . TGA curves of the gel precursor for two series depicted that the loss of residual organic groups and NO3 groups occurs below 450℃. According to the XRD patterns, the major diffraction peaks of the MgSiO3 and Mg2SiO4 series are consistent with a proto-enstatite structure (JCPDS No.11-0273) and a forsterite structure (JCPDS No.85-1364) respectively. With the excitation at 415 nm, the red emission band of Mn2+ ions is peaked at 661 nm for MgSiO3:1%(atom fraction) Mn2+ or 644 nm for MgiSiO4: 1 %(atom fraction) Mn2+ . Compared with Mg2SiO4:Mn2+ samples, MgSiO3:Mn2+ samples exhibit higher luminescence intensity and higher quenching concentration. In addition, the two series co-doped with Eu2+ , Dy3+ , Mn2+ were also prepared. Photo-luminescence and afterglow properties of the two co-doped series were analyzed, which show that MgSiO3: Eu2 + , Dy3+ , Mn2+ is more suitable for a red long-lasting phosphor.更多还原