【摘要】 制备了掺铒的玻璃样品TeO2-WO3-La2O3．测试了样品的吸收光谱、荧光光谱以及玻璃的热稳定性．应用Judd-Ofelt理论计算了玻璃的三个强度参数Ωt(t=2、4、6),电偶极跃迁谱线强度以及磁偶极跃迁谱线强度,分析了强度参数Ω2和玻璃成分变化的关系．应用 McCumber理论计算了Er3+在1．5μm处的受激发射截面．TeO2-WO3-La2O3玻璃在La2O3 的含量>5mol％时,未发现析晶开始温度(Tx),说明这种玻璃材料适合于光纤的拉制．研究结果表明TeO2-WO3-La2O3是制备宽带光纤放大器的理想基质材料．更多还原

【Abstract】 Er3+-codoped TeO2-WO3-La2O3 glasses were prepared. The thermal stability and spectral properties, such as absorption spectra, emission spectra of the glass samples were measured and investigated. Three intensity parameters, electric dipole transition, magnetic dipole transitions were calculated by Judd-Ofelt theory. The relationship of Ω2 and glass composition was analyzed. The emission cross-section of the 4I13/2 →4I15/2 transition of Er3+ ions was calculated by McCumber theory. When La2O3 content was up to 5mol%, glass samples showed no onset crystallization temperature (Tx), indicating that they are saitable for fiber drawing. The results show that TeO2-WO3-La2O3 glass has a good thermal stability and will be a promising host material for 1.5μm broadband amplification.更多还原