【摘要】 采用铝热快速凝固工艺制备了FeNiCr合金及TiC／FeNiCr复合材料,利用光学显微镜、扫描电镜、X射线衍射等手段研究了该复合材料的显微组织和相结构,测量了复合材料的压缩强度。结果表明,TiC／FeNiCr复合材料由TiC陶瓷增强相和α-Fe合金基体组成。TiC／FeNiCr复合材料组织细小,TiC呈多边形均匀分布在合金基体中,晶粒尺寸约为2-3μm。TiC对FeNiCr基体具有很好的晶粒细化及强化作用,TiC／FeNiCr的压缩断裂强度及形变率分别为2 760MPa及25％,远大于FeNiCr合金及部分Fe基非晶材料。更多还原

【Abstract】 The FeNiCr alloy and TiC/FeNiCr composites were prepared by the rapid solidification thermite process. The microstructure and the phase structure of the FeNiCr alloy and TiC/FeNiCr composites were investigated by means of OM, SEM and XRD. The compressive property of the composite was measured. Results show that the TiC and α-Fe are the only two phases in the TiC/FeNiCr composite. The TiC particles take the shape of polygon and are distributed uniformly in the composite. The grain size of the α -Fe matrix is notablely refined and the mechanical property is significantly reinforced by the TiC particles. The compressive fracture strength and compressibility of the TiC/FeNiCr are 2 760MPa and 25%, respectively, which are greatly improved than those of the FeNiCr alloy and some of Fe-based glass.更多还原