酚醛树脂的SiO2纳米复合对摩擦材料性能的影响
Influence on Rubing Material Performance of SiO2 Nanometer Compounds of Phenol Aldehyde Resin
【摘要】 在桐油改性酚醛树脂(TPF)的聚合过程中,添加经过分散的SiO2纳米粒子,制备成复合改性的热固性NT-PF,经过SETARAM TG-DSC92-16热分析仪测试NTPF的耐热性有明显的提高。将NTPF用于摩擦材料,按照相关标准在DMS-1定速摩擦磨损试验机上进行摩擦磨损对比试验,其抗热衰退性和摩阻性能具有明显的改善,材料的总磨损量下降,但在250℃存在一个磨损率峰值。从机理上对其摩擦磨损性能的改善作出了解释。
【Abstract】 In the course of polymerization of tung oil modified phenol aldehyde resin,by adding some SiO2 nanometer particles which have been scattered,compound modified heat-curable NTPF was made.The heat resistance performance of NTPF is obvious improved through the test of SETARAM TG-DSC92-16 hot analysis instrument.Its heat resistant and rub hinder performance is obvious improved and the whole wear and tear quantum of the material drop,but a wearing and tearing rate peak value exists at 250 ℃ when NTPF is used as rub material to do wear and tear comparing test in define rapid wear and tear machine DMS-1 according to relevant standard.Accordingly,the improvement of its wearing and tearing performance is analyzed from mechanism.
【Key words】 phenol aldehyde resin; nanometer compounds; rub materials; hot decline;
- 【文献出处】 润滑与密封 ,Lubrication Engineering , 编辑部邮箱 ,2006年08期
- 【分类号】TB383.1
- 【被引频次】30
- 【下载频次】274