近化学计量比铌酸锂晶体组分测定与缺陷观察

Determination of Composition and Observation of Defects of Near-stoichiometric Lithium Niobate Crystal

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 HUANG Qing-jie~1,WANG Ji-yang~2(1.School of Information Science and Engineering,Shandong University,Jinan 250100,China;2.State Key Laboratory of Crystal Materials,Shandong University,Jinan 250100,China)

【机构】山东大学信息科学与工程学院；山东大学晶体材料国家重点实验室济南250100；济南250100；

【摘要】采用助熔剂提拉法生长得到近化学计量比L iNbO3晶体。用多种方法测定了晶体组分,结果表明生长得到的晶体中[L i2O]含量为49.80%摩尔分数;对晶体缺陷的研究表明晶体质量有待提高,并分析了晶体中出现包裹物的原因。更多还原

【Abstract】 Near-stoichiometric LiNbO₃ crystal was grown from a melt with addition of K₂O by using Czochralski method.Different methods were used to determine the crystal composition.These measurements indicate that there is 49.8mol% Li₂O content in the crystal.Investigation of crystal defects reveals the crystal quality could be improved.The reason of inclusion that exists in the crystal is explained.更多还原

【关键词】 LiNbO₃；近化学计量比；缺陷；组分测定；化学腐蚀；
【Key words】 LiNbO₃； near-stoichiometric； defects； determination of composition； chemical etching；