稀土六方Z型铁氧体Ba3-xLaxCo2Fe24O41的合成及电磁性能与吸波特性
Electromagnetic properties and microwave absorbing property of Z type hexaferrite Ba3-xLaxCo2Fe24O41
【摘要】 利用柠檬酸溶胶-凝胶法合成了掺杂稀土La3+的磁铅石型系列Z型铁氧体,确定了稀土六方铁氧体Ba3-xLaxCo2Fe24O41中La3+的最大掺杂摩尔分数,并对其电磁特性及吸波特性进行了表征。结果表明:稀土La3+的最大掺杂摩尔分数x为0.30,实验发现随着La3+的加入,降低了Co2Z铁氧体的磁化强度、矫顽力,改善了材料的磁性;在2.0—10.0 GHz的频率范围内,吸波性能随着La3+量的增加而提高。
【Abstract】 The particles of Z type Hexaferrite Ba3-xLaxCo2Fe24O41 doped with Lanthanum were synthesized through a sol-gel method.The maximum mole fraction of La3+ was determined and electromagnetic property and microwave absorbing property of particles were studied.The maximum mole fraction of x for La3+ is 0.30.The magnetic properties are improved due to the addition of La3+,and the microwave absorbency is better as the increase of La3+ amount from 2.0 GHz to 10.0 GHz for the series of particles doped lanthanum.
【关键词】 材料检测与分析技术；
溶胶-凝胶法；
稀土六方铁氧体；
电磁性能；
吸波特性；
【Key words】 materials examination and analysis； sol-gel method； Z type hexaferrite doped lanthanum； electromagnetic property； microwave absorbing property；
【Key words】 materials examination and analysis； sol-gel method； Z type hexaferrite doped lanthanum； electromagnetic property； microwave absorbing property；
【基金】 吉林省自然科学基金资助项目(20000512-2);中国科学院长春应用化学研究所国家稀土重点开放实验室资助项目(R020202K)
- 【文献出处】 吉林大学学报(工学版) ,Journal of Jilin University(Engineering and Technology Edition) , 编辑部邮箱 ,2006年06期
- 【分类号】TM277
- 【被引频次】18
- 【下载频次】270