【摘要】 以聚苯胺和掺锑的氧化锡作为主要原料,采用溶胶-凝胶法制备了新型有机-无机杂化透明导电薄膜.薄膜的可见光透过率为85%以上,电导率达到100～101S·cm-1.研究了聚苯胺含量的变化对浸涂液粘度、薄膜结构、光透过率、电导率的影响.随着聚苯胺引入量的增加,薄膜的电导率、可见光透过率均有所增大.浸涂液的粘度可在长达25天的时间内保持稳定,很适于浸涂工艺.扫描电镜照片显示,薄膜比较致密、均匀,厚度为250nm左右.更多还原

【Abstract】 New organic-inorganic hybrid films with relative high conductivity and good optical transmittance were successfully synthesized by polymerization of antimony-doped tin oxide in the presence of polyaniline via a sol-gel route. Visible light transmittance of the obtained film was over 85%, and its conductivity reached 100～101 S·cm-1. The effect of content of PANI on viscosity of dipping solution, structure, transmittance and conductivity of the hybrid films was investigated. Conductivity and visible light transmittance of the films were increased with the increase of PANI content. The viscosity of the dipping solutions was almost unchanged during 25 d, which was much suitable for a dip-coating process. The dense and uniform film with a thickness of ～250 nm was observed from SEM photographs.更多还原