【摘要】 研究了新型SiC复合陶瓷的冲蚀行为,并与45碳钢、铸钢和Al₂O₃陶瓷进行了比较．结果表明：45碳钢、铸钢和冲蚀率大都在0．13～0．26 mg/g范围内随着攻角变化,最大值分别出现在15°、30°、90°攻角,具有典型韧、脆性材料的特点；新型SiC复合陶瓷的抗冲蚀性能优越,特别是其冲蚀率几乎不随攻角变化（冲蚀率大约为0．025 mg/g,速度影响因子为1．3～1．8）．新型SiC复合陶瓷中软硬相的有效配合、凹凸不平的损伤表面、多粒度的多晶型SiC紧密结合和细小SiC颗粒的弥散强化对其优异抗冲蚀性能均起着重要的作用．更多还原

【Abstract】 The erosion behavior of a new SiC reinforced ceramic had been investigated by sand-blast test,as comparison with 1045 carbon steel,cast steel and Al₂O₃ ceramic.The results show that carbon steel,cast steel and Al₂O₃ ceramic reveal normal ductile/brittle erosion behavior with maximum erosion rate at 15°,30°and 90°impingement angles respectively and variation in the range of 0.13～0.26 mg/g. Erosion resistance of the SiC reinforced ceramic are super excelled to that of the others,especially,its erosion rates are scarcely changed at various impingement angles,all about 0.025 mg/g and its velocity index as 1.3～1.8.The outstanding performance on erosion resistant of the new SiC reinforced ceramic comes from the effect,such as valid match of soft/hard phase,irregularity of damage surface,tight cohesion among variant granularity particles of multi-crystal type SiC,dispersion strengthening by fine SiC particles.更多还原