硬脂酸改性Mg(OH)2的机理及对EVA性能的影响

Mechanistic studies of the effect of stearic acid coated Mg(OH)2 on properties of EVA/Mg(OH)2 composites

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具,请取消加速工具后下载。

【作者】 黄宏海田明梁文利张立群

【Author】 HUANG Hong-hai TIAN Ming LIANG Wen-li ZHANG Li-qun (Key Laboratory of Novel Polymer Materials Preparation and Processing of Beijing City,Beijing University of Chemical Technology,Beijing 100029,China).

【机构】 北京化工大学新型高分子材料制备与加工北京市重点实验室北京化工大学新型高分子材料制备与加工北京市重点实验室 北京100029北京100029

【摘要】 采用FTIR表征硬脂酸对氢氧化镁Mg(OH)2的改性效果,发现不存在一个所谓的“最佳量”,分析认为硬脂酸对Mg(OH)2表面改性既包括着硬脂酸—COOH与Mg(OH)2的—OH之间的弱酯化反应,也包含着酸与弱碱Mg(OH)2之间的酸碱反应,所以硬脂酸对Mg(OH)2的表面改性随硬脂酸用量增加而持续进行。此外,改性剂用量也对Mg(OH)2填充乙烯-醛酸乙烯酯共聚物(EVA)体系性能存在显著的影响。与填充未处理Mg(OH)2体系相比较,表面改性剂用量的增加会导致复合材料的拉伸强度的不断下降,断裂伸长率的增加和阻燃性能的急剧恶化。但是,复合材料的表观黏度下降,加工性能得到改善。

【Abstract】 In this paper,FTIR spectroscopy was employed to evaluate the effect on Mg(OH)2 of coating the surface with stearic acid.It was found that there was no one optimum loading.It is proposed that the surface modification involves two important processes: one is a type of weak esterification and the other is the acid-base interaction between stearic acid and Mg(OH)2.Both these reactions were favored by increasing the amount of stearic acid.Moreover,the amount of surface modifier had a significant influence on the properties of EVA/Mg(OH)2 composites.A continuous decrease in tensile strength and increase in elongation at break of the composites were observed with increasing amount of stearic acid.Meanwhile the flame retardancy of the composites was poorer however compared with that of composites filled with uncoated Mg(OH)2.However,surface modification of Mg(OH)2 by stearic acid facilitated the processing of the composites.

【基金】 北京市自然科学基金重点课题(231001);北京市科技新星计划(H010410010112);北京市教委重点学科建设基金(SYS100100420)
  • 【文献出处】 北京化工大学学报(自然科学版) ,Journal of Beijing University of Chemical Technology(Natural Science Edition) , 编辑部邮箱 ,2006年02期
  • 【分类号】O614.22
  • 【被引频次】55
  • 【下载频次】814