【摘要】 采用功率为 2kW、扫描速度为 10 0mm/min的工艺参数对钻杆接头材料 30CrMnSiA钢进行了表面相变硬化处理 ,研究了相变层的组织和硬度特征。实验结果表明 ,30CrMnSiA钢表面相变硬化层分为完全淬硬层、过渡层和受热影响的基体组织 ,硬化层的显微组织明显细化 ,其表面层的硬度比高频淬火的硬度提高了 30 % ,淬硬层深度达 1 7mm ,比高频淬火深度提高近 1倍。更多还原

【Abstract】 Surface hardening of drill rod joint material 30CrMnSiA by using 2 kW power and 100 mm/min scanning velocity has been performed. The microstructure and hardness of the transformation layer have been studied. The experimental results show that the surface hardened layer consists of the hardened region and the interim region and the temper microstructure. The microstructure of hardened layer was very tiny. Its hardness is 30% higher than the high frequency quenched. Quenched depth is 1 7 mm and one time higher than the high frequency quenched更多还原