【摘要】 对 2种以 10 .5 ,12m/min快速铸轧的纯铝板进行了显微组织分析、力学性能测试和深冲性能试验 ,并与传统铸轧速度 (0 .9m/min)生产的纯铝板进行了比较。结果表明 ,快速铸轧铝带坯有较细的晶粒度、高的屈服强度和良好的深冲性能更多还原

【Abstract】 The microstructure mechanical performance and deep slash property of the casting aluminum strips produced at high casting speeds of 10.5 and 12 m/min were investigated. Compared with traditional casting aluminum strips produced at casting speed of 0.9 m/min. The results show that the casting aluminum strips produced at high casting speeds had finer grain size, higher yielding strength and better deep clash performance.更多还原